PCE104p Powder Polycarboxylate Superplaticizer for Gypsum-Based Products

• Customization: Available
• Appearance: Powder
• Application: Grouting Material, Mortar Admixture, Plastering Material, Self-Leveling Compound
• Model NO.: PCE-104P
• Chemical Composition: Polycarboxylate-based Water Reducers
• Setting Time: Controlled Extended
• Type: Ultra-high-range Water-reducing Agent
• Water Reduction Rate: ≥25%
• Color: White
• pH: 7-9(10% Aqueous Solution)
• Solid Content: ≥98%
• Moisture Content: ≤5.0%
• Cement Slurry Flowability: ≥220*0.95 mm
• Water Reduction Rate of Mortar: ≥25%
• Chloride Ion Content: ≤0.01%
• Initial Setting Time Diff.: -30 ± 10 Min
• Final Setting Time Diff.: -45 ± 15 Min
• Transport Package: 25 Kg / 55 Lb Paper Bag
• Trademark: Sidley
• Origin: Linyi City, Shandong Prov, China
• HS Code: 38244000

Product Description

FAQ

Why should you choose PCE ?

1. Unmatched Workability Retention

PCEs maintain slump for 90-120 minutes without segregation – critical for high-rise pours or congested sites. 

2. High-Density Reinforcement Penetration

When pouring seismic beams or column joints with rebar cages, PCE's low-viscosity/high-cohesion combo flows like water through tight spaces without blocking. 

3. True High-Strength Concrete Enablement

Want 80 MPa concrete without heat-curing? PCE's ≥25% water reduction (vs. SNF's 15% cap) creates near-zero bleed mix designs. 

4. Waste Reduction

Contractors save 3-5% on material costs with PCE. 

5. Compatibility with Modern Materials

6. Critical Failure Prevention

No catastrophic false set as no sulfates destroy dispersion. 

Conclusion

PCE superplasticizers represent 3rd-generation admixture technology, offering:

1.Unmatched water reduction → structural durability
2.Molecular tunability → application-specific optimization
3.Environmental compliance → global project eligibility

Product Description

PCE-104P

 PCE-104P is a powder Polycarboxylic Superplasticizer high-performance water reducing agent with very high water reduction rate, which 
is very suitable for all kinds of gypsum-based materials and ultra-low water-cement ratio cement-based materials.

Application

*Gypsum-based/cement-based self-leveling mortar 
*High strength grout for wind power generation 
*UHPC and GRG/GRC Precast Components 
*Repair mortar

Benifits in use

*Ultra-high water reduction and good plasticization, giving excellent fluidity of mortar 
*Excellent high temperature resistance, suitable for gypsum or mortar where the material itself is too hot or stored under high 
t*eSmtropn egradtuis rpee crosinndgita iobnilsit .y, fast plasticization, applicable to cementitious materials with ultra-low water-to-cement ratio 
**Good stability, low sensitivity, with a gentle water reduction growth curve

Usage Guidelines

*Ensure the product is thoroughly pre-mixed with other dry powder components before packaging. On-site, mix and use according to the 
specified water amount. 
*The recommended dosage is 0.1%-0.5% of the cementitious material, but it is essential to conduct pre-testing based on raw materials 
and construction specifications prior to use. 
*It is recommended to use with sodium gluconate, the water reduction rate will be higher and the loss of 30 minutes fluidity will be 
smaller. 
* Handling Instructions: Follow safety precautions such as wearing gloves and avoiding contact with eyes during handling

Storage Condition

*Store the product in its original packaging in a dry, clean environment, away from heat sources. While this product is not prone to losing 
efficacy, it is hydrophilic and may slowly absorb moisture if stored in poor conditions. 
*It is recommended to use the first-in, first-out principle. 
*Ensure the packaging is tightly sealed to prevent moisture absorption if not fully used.